Abstract:
Aluminium waste accumulated in landfills is a solid waste in abundance. Various methods have been employed
to alleviate the waste only to yield secondary pollution effects. This study seeks to provide an alternative greener
recycling procedure that is beneficial to society in terms of health and economics through energy storage materials. The study aimed to synthesize and characterize aluminium oxide nanoparticles from waste aluminium
foil and its potential applications in fabricating aluminium-ion cell, FAIC.1 Aluminium oxide nanoparticles were
obtained by co-precipitation of waste aluminium foils at constant annealing room temperature followed by
mechanical milling to nanoparticulate range. The particles were then characterized for particle size and phases
(X-ray diffraction), functional groups and optical activity (infra-red and ultra-violet-visible spectroscopy
respectively). Cell assembling of FAIC was done using a graphite anode while the cathode had a standard and the
synthesized aluminium oxide nanoparticles. Sulfuric acid and magnesium sulfate electrolytes were used with two
binders; polyacrylate and silicone adhesives. The average synthesis yield was 40.64 ± 19.69%. Most of the
particles had a α-Al2O3 and γ-Al2O3 phase with an average size of 63.763 nm and 66.5144 nm for the two
polymorphs respectively. There were several OH-groups coupled to Al–O bonds. The optimal absorption peak
was λmax = 237 nm corresponding to a band gap of 5.25eV. The synthesized nanoparticles exhibited great
electrochemical potential, nearing the standard one in most of the parameters. The FAIC potential, current,
power densities and polarization curves from sulfuric acid electrolyte and polyacrylate binder were significantly
higher to those of magnesium sulfate and silicone binder (P > 0.05).