Abstract:
Metal contacts on clean, hydrogenated and oxygenated diamond surfaces have been studied using ab initio
Density Functional Theory (DFT). Five metals, i.e., gold, titanium, tantalum, vanadium and palladium on the
three surfaces were considered. Gold and palladium were found to form weak bonds on clean, hydrogenated
or oxygenated diamond (111) surfaces compared to the other three metals. Bulk properties were also studied
following the formation of the respective ohmic contacts on the three surfaces. The clean diamond surface
was found to have surface states which were modified by oxygen but removed by hydrogen. Density of states
studies revealed that all the investigated metals had an effect on the electrical properties of the diamond sur-
face. A peak that was characteristic of diamond was observed at ≈−11.8 eV. For the clean diamond surface
terminated with gold and palladium, states due to Au-2p orbitals were observed at − 2.5 eV and
≈−1.5 eV, while Pd-5s orbitals were located at ≈−1.7 eV and − 0.5 eV on the same surface. Titanium, tan-
talum and vanadium showed unique states at high binding energies of ≈−38 eV for vanadium, ≈−34 eV for
tantalum and ≈−32.5 eV for titanium, which were thought to be responsible for their strong bonding.